Technical specifications
Technical Properties of Wood Composite
| Ominaisuus | Testimenetelmä | Arvo | Yksikkö |
|---|---|---|---|
| Density | ASTM D792-2008 METHOD B | 1,285 | G/CM3 |
| Flexural Strength | ASTM D790-07E1 | 370 | Mpa |
| Flexural Modulus | ASTM D790-07E1 | 38 | Mpa |
| Tensile Strength | ASTM D638-08 | 21,08 | Mpa |
| Water Absorption | ASTM D570-98 | 0,8 | % |
| Longitudinal Thermal Expansion | TMA | 49,82 | UM/M °C |
| IZOD Impact Strength | ASTM D4812-06 | 79 | J/M |
| Hardness | ASTM D2240-05 | D/76/1 | |
| Flexural Strength | ASTM D790 | ≥12 | Mpa |
| Horizontal Burning | UL 94-1996REV.9:2006 SECTION 7 | 22 | MM/MIN |
| Torsional Stiffness | ASTM D790 | ≥1600 | Mpa |
| Compressive Strength | ASTM D143 | ≥30 | Mpa |
| Nail Holding Strength | ASTM D1037 | ≥3000 | N |
| Nail Withdrawal Strength | ASTM D1761 | 802 | psi |
| Recovery | ASTM D7032-SECTION 5.4 | 82,66 | % |
| Heat Deflection | ASTM D648 | ≥100 | °C |
| UV Resistance (Light Fastness/Xenon-Arc Exposure) | IS0105-02:2000/Amd.2:2000(E), ISO 105-A02:1993 Cor2:2005, altistamisaika 720 tuntia | Gray 4-5, Brown 4, Teak 4-5 Dark Walnut 4-5 | |
| Heat Shock Test | IEC 60068-2-14 Na: 1986, 5 sykliä | No cracking, warping, chipping, or color change | |
| Slip Friction (measurement in horizontal direction | ASTM F 609 | Friction index 6,63 | |
| Material Composition | Recycled Plastic: 35% Natural Fibers: 60% Additives: 5% |